Formation of bulk metallic glass in situ nanocomposite in (Cu50Zr43Al7)99Si1 alloy
2015-10-31 14:51  

M. Malekan, S.G. Shabestari, W. Zhang, S.H. Seyedein, R. Gholamipour, K. Yubuta, A. Makino andA. Inoue,  Mater. Sci. Eng. A, 553 (2012), 10-13.

Abstract

The structure and mechanical properties of the bulk (Cu50Zr43Al7)99Si1 (at.%) rods with different diameters prepared by copper mold casting are investigated. It was found that the alloy with diameter of 2 mm has a fully glassy structure. The nanocrystals with the sizes ranging from 2 to 10 nm distributed in the glassy matrix for the alloy rod with a diameter of 3 mm, and the successful synthesis of the (Cu50Zr43Al7)99Si1 bulk metallic glass in situ nanocomposite was obtained. High compressive strength of 1969 MPa and limited plastic strain of less than 1% were obtained for the 2 mm (Cu50Zr43Al7)99Si1 glassy rod. For the 3 mm alloy rod, the compressive strength and plastic strain are 1835 MPa and 10%, respectively. The CuZr nanocrystalline phase precipitated from the 3 mm (Cu50Zr43Al7)99Si1 rod shows evident plastic deformation, which contributes to the high ductility of the (Cu50Zr43Al7)99Si1 bulk metallic glass in situ nanocomposites.

详细

关闭窗口
 
 
 
 返回首页 | 网站地图 | 联系我们 | 管理登录 

大连理工大学非晶及纳米晶功能材料研究室  地址:辽宁省大连市大连理工大学材料科学与工程学院
电话:0411-84706400  邮编:116024