Proton conductive inorganic–organic hybrid membranes functionalized with phosphonic acid for polymer electrolyte fuel cell
2015-08-15 22:11  

Umeda, J., Suzuki, M., Kato, M., Moriya, M., Sakamoto, W., & Yogo, T. (2010). Journal of Power Sources, 195(18), 5882-5888.

Abstract

Inorganic–organic hybrid membranes composed of Si–O networks and an aliphatic main-chain polymer backbone were synthesized from an alkoxysilane derivative and an F-substituted phenylvinylphosphonic acid via copolymerization and sol–gel reaction. Thus, (trimethoxysilylmethyl)styrene (TMSMS) was copolymerized with 3-fluorophenyl- vinylphosphonic acid (FC6H4VPA), and the product was hydrolyzed to afford an inorganic–organic hybrid composite. Spectroscopic analysis revealed that the inorganic–organic hybrid structure was constructed via the polymerization of TMSMS and FC6H4VPA and the condensation of methoxy-Si bonds. The membranes showed good thermal stability up to 180 °C, and it was found that the aliphatic chains bound to the F-substituted aromatic rings and the Si–O linkages in the hybrid membranes improved their mechanical properties. In addition, the proton conductivity of the membranes depended on the P/Si ratio of the product and increased as the P content increased. Notably, the conductivity at 130 °C for the hybrid membrane synthesized with a TMSMS/FC6H4VPA ratio of 1/6 was 1.6×10−3 S cm−1 and 6.4×10−2 S cm−1 at low and 100% relative humidity (RH), respectively, while its power density at 140 °C and 30% RH was 3.0 mW/cm2.

详细

关闭窗口
 
 
 
 返回首页 | 网站地图 | 联系我们 | 管理登录 

大连理工大学非晶及纳米晶功能材料研究室  地址:辽宁省大连市大连理工大学材料科学与工程学院
电话:0411-84706400  邮编:116024